ASTM A240/A240M Standard Specification for Chromium and Chromium-Nickel Stainless Steel Plate, Sheet, and Strip for Pressure Vessels and for General Applications. Duplex (Austenitic-Ferritic) steel Type: 2205 UNS Designation : S32205 Chemical Composition Requirements, %, Max. C: 0.030 Mn: 2.00 P: 0.030 S: 0.020 Si: 1.00 Cr: 22.0-23.0 Ni: 4.5-6.5 Mo:3.0-3.5 N: 0.14-0.20 Mechanical…
4140 WROUGHT CHROMIUM-MOLYBDENUM LOW ALLOY STEELS WITH 80 KSI 1.0 Scope 1.1 This specification is for seamless 4140 API 5CT chromium-molybdenum low alloy steels in quenched and tempered condition with 80 ksi MYS. 1.2 Material is to conform to the requirements of NACE MR0175 (ISO 15156-2) and is resistant to Sulfide Stress Cracking (SSC) in H2S containing…
BS EN 10253-2:2007 Butt-welding pipe fittings — Part 2: Non alloy and ferritic alloy steels with specific inspection requirements Steel grade: 10CrMo9-10 Heat treatment condition: NT (Normalized and tempered) it may be necessary in the case of wall thickness T above 25 mm or T/D > 0,15 to apply quenching and tempering in order to achieve…
S355J0 BS EN 10025-2:2004 Hot rolled products of structural steels Part 2: Technical delivery conditions for non-alloy structural steels Chemical composition of the ladle analysis of S355J0 Chemical composition of the prduct analysis of S355J0 Maximum CEV based on the ladle analysis of S355J0 Mechanical properties of S355J0 impact strength KV longitudinal S355J0
ASTM A 182 Forged or Rolled Alloy and Stainless Steel Pipe Flanges, Forged Fittings, and Valves and Parts for High-Temperature Service Grade F904L (Austenitic Stainless Steels) Chemical Requirements: Composition, %, max C: 0.020 Mn:2.00 P: ≤0.040 S: ≤0.030 Si: 1.00 Cr: 19.0-23.0 Ni:23.0-28.0 Mo: 4.0-5.0 Cu:1.00-2.00 N: 0.10 Austenitizing/Solutioning Temperature: 1040 °C – 1150℃ Cooling Media: Liquid Quenching Cool Below ℃ 260…
ASTM A 182 Forged or Rolled Alloy and Stainless Steel Pipe Flanges, Forged Fittings, and Valves and Parts for High-Temperature Service Grade F48 (Austenitic Stainless Steels) Chemical Requirements: Composition, %, max C: 0.030 Mn:2.00 P: ≤0.045 S: ≤0.030 Si: 0.75 Cr: 17.0-20.0 Ni:13.5-17.5 Mo: 4.0-5.0 N: 0.10-0.20 Austenitizing/Solutioning Temperature, min: 1040 °C Cooling Media: Liquid Quenching Cool Below ℃ 260 Tensile…
ASTM A 312 Seamless, Welded, and Heavily Cold Worked Austenitic Stainless Steel Pipes UNS Designation N08904 Chemical Requirements: Composition, %, max C: 0.020 Mn:2.00 P: ≤0.040 S: ≤0.030 Si: 1.00 Cr: 19.0-23.0 Ni:23.0-28.0 Mo: 4.0-5.0 N: 0.10 Cu: 1.00-2.00 Heat Treating Temperature: 1100 °C Tensile Requirements Tensile Strength, min.: 490MPa Yield Strength, min.: 215MPa Elongation in 2…
ASTM A 312 Seamless, Welded, and Heavily Cold Worked Austenitic Stainless Steel Pipes UNS Designation S31726 Chemical Requirements: Composition, %, max C: 0.03 Mn:2.00 P: ≤0.040 * S: ≤0.030 Si: 1.00 Cr: 17.0-20.0 Ni:14.5-17.5 Mo: 4.0-5.0 N: 0.10-0.20 Cu: 0.75 *For welded pipe, the phosphorus maximum shall be 0.045 %. Heat Treating Temperature: 1040 °C Tensile Requirements Tensile Strength,…
ASTM A240/A240M Standard Specification for Chromium and Chromium-Nickel Stainless Steel Plate, Sheet, and Strip for Pressure Vessels and for General Applications. Type: 410 UNS Designation : 41000 Chemical Composition Requirements, %, Max. C: 0.08-0.15 Mn: 1.00 P: 0.040 S: 0.030 Si: 1.00 Cr: 11.5-13.5 Ni: 0.75 Mechanical Test Requirements Tensile Strength, min: 450Mpa Yield Strength,…
ASTM A537 Standard Specification for Pressure Vessel Plates, Heat-Treated, Carbon-Manganese-Silicon Steel This specification covers heat-treated carbon-manganese-silicon steel plates intended for fusion welded pressure vessels and structures. Material under this specification is available in the following three classes: Class Heat Treatment Thickness Yield Strength, min, Tensile Strength, min, ksi (MPa) ksi (MPa) 1 Normalized ≤2.5in.( ≤65mm) 50…