ASTM B148 – Aluminum-Bronze Sand Castings Chemical Requirements Composition, % Classification Copper Alloy UNS No. Copper Aluminum Iron Manganese Nickel (incl cobalt Silicon Lead Aluminum Bronze C95200 86.0 min 8.5–9.5 2.5–4.0 … … … … Aluminum Bronze C95300 86.0 min 9.0–11.0 0.8–1.5 … … … … Aluminum Bronze C95400 83.0 min 10.0–11.5 3.0–5.0 0.50 max…
ASTM A333 – Seamless and Welded Steel Pipe for Low Temperature Service Chemical Requirements (max, %) Grade C Mn P S Si Ni Cr Cu Al V Nb Mo Co 1 (Note) 0.30 0.40-1.06 0.025 0.025 … … … … … … … … … 3 0.19 0.31-0.64 0.025 0.025 0.18-0.37 3.18-3.82 … … ……
ASTM A860 – Wrought High-Strength Low-Alloy Steel Butt-Welding Fittings Grade: WPHY42 WPHY46 WPHY52 WPHY60 WPHY65 WPHY70 Chemical Compositions (max, %) Heat analysis C Mn P S Si Ni Cr Mo Cu Ti V Cb V+Cb Al 0.20 1.00-1.45 0.030 0.010 0.15-0.40 0.50 0.30 0.25 0.35 0.05 0.10 0.04 0.12 0.06 1.The carbon equivalent as calculated by…
ASTM A 519 – Seamless Carbon and Alloy Steel Mechanical Tubing ASTM A 519 covers several grades of carbon and alloy steel seamless mechanical tubing. When welding is used for joining the weldable mechanical tube grades, the welding procedure shall be suitable for the grade, the condition of the components,and the intended service. This specification covers both…
ASTM A694 – Carbon and Alloy Steel Forgings for Pipe Flanges, Fittings, Valves, and Parts for High-Pressure Transmission Service Chemical Compositions (max, %) C Mn P S Si Heat Analysis 0.26 1.40 0.025 0.025 0.15-0.35 Product Analysis 0.265 1.44 0.030 0.030 0.10-0.40 Mechanical Properties (min ) Grade Tensile Strength MPa Yield Strength MPa Elongation in 2 in. or…
ASTM A53 – Pipe, Steel, Black and Hot-Dipped, Zinc-Coated, Welded and Seamless Chemical Compositions（max%） Grade C Mn P S Cr Cu Mo Ni V Type S (seamless pipe) A 0.25 0.95 0.05 0.045 0.4 0.4 0.15 0.4 0.08 B 0.3 1.2 0.05 0.045 0.4 0.4 0.15 0.4 0.08 Type E (electric-resistance-welded) A 0.25 0.95 0.05…
ASTM A106 – Seamless Carbon Steel Pipe for High-Temperature Service Chemical Compositions (max%) Grade C Mn P S Si Cr Cu Mo Ni V A 0.25 0.27-0.93 0.035 0.035 ≥0.10 0.40 0.40 0.15 0.40 0.08 B 0.30 0.29-1.06 0.035 0.035 ≥0.10 0.40 0.40 0.15 0.40 0.08 C 0.35 0.29-1.06 0.035 0.035 ≥0.10 0.40 0.40 0.15 0.40…
ASTM A105 – Carbon Steel Forgings for Piping Applications Chemical Compositions (max, %) C 0.35 Mn 0.60-1.05 P 0.035 S 0.040 Si 0.10-0.35 Cr 0.30 Cu 0.40 Mo 0.12 Ni 0.40 V 0.08 Notes: 1) For each reduction of 0.01% below the specified C maximum(0.35%), an increase of 0.06% Mn above the specified maximum (1.05%) will be permitted up to…