ASTM A335 – Seamless Ferritic Alloy-Steel Pipe for High-Temperature Service
Grade: P22
Chemical Requirements max %
| Elements | Composition |
| Carbon | 0.05 – 0.15 |
| Manganese | 0.30–0.60 |
| Phosphorus | 0.025 |
| Sulfur | 0.025 |
| Silicon | 0.50 |
| Chromium | 1.90 – 2.60 |
| Molybdenum | 0.87 – 1.13 |
Tensile Requirements
| Tensile strength, min ksi[Mpa] | 60[415] |
| Yield strength, min: ksi[Mpa] | 30[205] |
Elongation Requirements
| Longitudinal | Transverse | |
| Elongation in 2 in. or 50 mm, (or 4D), min, %: Basic minimum elongation for wall 5.16 in. [8 mm] and over in thickness, strip tests,and for all small sizes tested in full section | 30 | 20 |
| When standard round 2-in. or 50 mm gage length or proportionally smaller size specimen with the gage length equal to 4DB 4 times the diameter) is used | 22 | 14 |
| For strip tests a deduction for each 1.32in. [0.8 mm] decrease in wall thickness below in. [8 mm] from the basic minimum elongation of the following percentage points shall be made | 1.50 A | 1.00 A |
A Table below gives the calculated minimum values.
| Wall Thickness | Longitudinal | Transverse | |
| in. | mm | ||
| 5 ⁄ 16 (0.312) | 8 | 30 | 20 |
| 9 ⁄ 32 (0.281) | 7.2 | 28 | 19 |
| 1 ⁄ 4 (0.250) | 6.4 | 27 | 18 |
| 7 ⁄ 32 (0.219) | 5.6 | 26 | … |
| 3 ⁄ 16 (0.188) | 4.8 | 24 | … |
| 5 ⁄ 32 (0.156) | 4 | 22 | … |
| 1 ⁄ 8 (0.125) | 3.2 | 21 | … |
| 3 ⁄ 32 (0.094) | 2.4 | 20 | … |
| 1 ⁄ 16 (0.062) | 1.6 | 18 | … |